6013 aluminium alloy

Alloy of aluminum

6013 aluminium alloy consist of magnesium, silicon, copper, manganese, iron, zinc, chromium, and titanium as minor alloying elements.[1]

Chemical Composition

Element [1] Weight percentage (%)
Aluminum, Al 94.8-97.8
Magnesium, Mg 0.80-1.2
Silicon, Si 0.60-1
Copper, Cu 0.60-1.1
Manganese, Mn 0.20-0.80
Iron, Fe ≤ 0.50
Zinc, Zn ≤ 0.25
Chromium, Cr ≤ 0.10
Titanium, Ti ≤ 0.10
Remainder (each) ≤ 0.15
Remainder (total) ≤ 0.050

Mechanical Properties

Properties [1] Values
Tensile strength ≥ 392 MPa
Yield strength ≥ 379 MPa
Elongation at break ≥ 5%
Young's Modulus [2] 69 GPa
Fatigue Strength [2] 98 to 140 MPa

Applications

  1. Valves
  2. Machine parts
  3. Munitions
  4. ABS Braking systems
  5. Hydraulic applications
  6. Roller blade parts

[1]

References

  1. ^ a b c d "6013 aluminium alloy properties". 25 April 2013. Archived from the original on 2016-09-14.
  2. ^ a b "6013 Aluminium alloy properties". Archived from the original on 2016-11-14.
  • v
  • t
  • e
Aluminium alloys
Introduction
  • Aluminium
  • Aluminium alloys
  • History of aluminium
Al 1000 series (pure)
  • 1050
  • 1060
  • 1070
  • 1100
  • 1145
  • 1199
  • 1200
  • 1230
  • 1350
  • 1370
  • 1420
  • 1421
  • 1424
  • 1430
  • 1440
  • 1441
  • 1445
  • 1450
  • 1460
  • 1461
  • 1464
  • 1469
Al-Cu 2000 series
Al-Mn 3000 series
Al-Si 4000 series
  • 4006
  • 4007
  • 4015
  • 4032
  • 4043
  • 4047
  • 4543
Al-Mg 5000 series
Al-Mg-Si 6000 series
Al-Zn 7000 series8000 series (misc.)
  • 8006
  • 8009
  • 8011
  • 8014
  • 8019
  • 8025
  • 8030
  • 8090
  • 8091
  • 8093
  • 8176
Named alloys